Title: Novel applications for paper sludge ash
Authors: Spathi, Charikleia
Item Type: Thesis or dissertation
Abstract: The disposal of paper sludge ash (PSA) generated by the UK paper industry has caused environmental concerns and there is a need to provide more sustainable management options as an alternative to landfill. This study investigated and developed viable technologies for the production of waste-derived lightweight filler (LWF) particles with high strength-to-density ratios and hydrophobic materials. Two types of PSA, supplied by Aylesford Newsprint and UPM-Shotton recycled paper mills, were processed into LWFs and hydrophobic powders. They were both composed of gehlenite (Ca2Al2SiO7), calcite (CaCO3), calcium silicate (a’– Ca2SiO4), lime (CaO) and quartz (SiO2). Given that PSA exhibited low sintering reactivity at temperatures up to 1200 °C, recycled soda-lime glass was used to promote sintering while minimising the energy intensity of the proposed thermal treatment. Wet-milling of glass with PSA addition up to 20 wt. % produced foamed lightweight materials (~1 g˙cm-3) after rapid sintering at 800 °C. This was shown to be because of extensive growth of pores caused by gas evolution from the decomposition of, primarily, calcium carbonate present in PSA. Thermodynamic considerations for the 80/20 glass/PSA system also showed that the amount of gas evolved and entrapped within the sintered body determined the extent of closed-cell porosity for mixes of given viscosity and particle size characteristics. This was found to be a time-sensitive mechanism on a minutes scale. Incorporation of such low water permeability LWFs in cement mortars corroborated their use as structural, thermal-insulating materials. Dry milling of PSA particles with stearic acid led to unexpected surface functionalization inducing super-hydrophobicity. Both PSA samples exhibited water contact angles in the region of 150° when treated with 4 wt. % of stearic acid under optimised process conditions. This was due to the formation of calcium stearate self-assembling layers physically and chemically adsorbed on fracture PSA surfaces. PSA particles exhibited higher hydrophobicity when treated with stearic acid compared to other inorganic substrates and organic acids investigated. Research findings indicate that manufacturing of glass/PSA LWFs and PSA-based hydrophobic materials was technically feasible at laboratory scale. Economic and environmental benefits could drive commercial exploitation of research outputs.
Content Version: Open Access
Issue Date: Nov-2015
Date Awarded: Mar-2016
URI: http://hdl.handle.net/10044/1/31599
DOI: https://doi.org/10.25560/31599
Supervisor: Cheeseman, Chris
Vandeperre, Luc
Sponsor/Funder: Engineering and Physical Sciences Research Council
Funder's Grant Number: CCIEW-NN0563-151620
Department: Civil and Environmental Engineering
Publisher: Imperial College London
Qualification Level: Doctoral
Qualification Name: Doctor of Philosophy (PhD)
Appears in Collections:Civil and Environmental Engineering PhD theses

Unless otherwise indicated, items in Spiral are protected by copyright and are licensed under a Creative Commons Attribution NonCommercial NoDerivatives License.

Creative Commons