An Investigation, Using Standard Experimental Techniques, to Determine FLCs at Elevated Temperature for Aluminium Alloys

Abstract

An experimental procedure has been developed for the determination of FLCs at elevated temperatures. The GOM ARGUS system was employed for measuring surface strain based on pre-applied grids (pattern), and limit strains were determined according to the ISO 12004-2:2008 standard. Forming limit curves (FLCs) have been determined for AA5754 under warm forming conditions in an isothermal environment. The tests were carried out at various temperatures up to 300oC and forming speeds ranging from 5 – 300 mm s-1 . Results reveal the significant effect of both temperature and forming speed on FLCs of AA5754. Formability increases with increasing temperature above 200oC. Formability also increases with decreasing speed. The presented FLC results show that the best formability exists at low forming speed and the high temperature end of the warm forming range.