Experimental investigation of the air blast performance of hybrid composite skinned sandwich panels with X-ray micro-CT damage assessment
File(s)
Published version
Author(s)
Type
Journal Article
Abstract
This research investigates the performance of interlaminar hybrid composites as the skins of composite sandwich panels under blast loading with the aim of promoting delamination between dissimilar plies for energy absorption. The deformation of the composite panels was captured using high-speed digital image correlation (DIC). High-speed full-field DIC enables failure to be captured at the moment it occurs across the entire panel. X-ray micro-CT imaging was used to assess the post-blast damage sustained by particular areas of interest from each panel, which were selected based on DIC results. The combination of full-field DIC and detailed X-ray micro-CT scanning enabled a unique comparison of both the global and localised blast resilience of hybrid and conventional composite sandwich panels to be performed.
Following a single blast load, the extent of damage to the Hybrid-3B skinned sandwich panel was found to lie between that of GFRP and CFRP skinned sandwich panels. X-ray micro-CT scanning of these panels reveals that there is no continuous damage path through the skin thickness of Hybrid-3B, whereas the GFRP and CFRP panels sustain damage in every ply.
Following repeat blast loading, the Hybrid-4 skinned sandwich panel suffered from a front skin crack spanning the length of the panel. Post-blast compressive strength testing reveals that this skin crack and resulting core crack acted as a stress relief, limiting the damage sustained elsewhere in the panel.
It was concluded that Hybrid-3B results in a good trade-off between strength and stiffness and is advantageous over conventional CFRP and GFRP panels under a single blast load. Under repeated loading Hybrid-4 offers advantages over Hybrid-3B. Finally, the design of the support structure can significantly aid in blast resilience, and, a holistic approach considering both panels and support should be taken when designing for blast resilience.
Following a single blast load, the extent of damage to the Hybrid-3B skinned sandwich panel was found to lie between that of GFRP and CFRP skinned sandwich panels. X-ray micro-CT scanning of these panels reveals that there is no continuous damage path through the skin thickness of Hybrid-3B, whereas the GFRP and CFRP panels sustain damage in every ply.
Following repeat blast loading, the Hybrid-4 skinned sandwich panel suffered from a front skin crack spanning the length of the panel. Post-blast compressive strength testing reveals that this skin crack and resulting core crack acted as a stress relief, limiting the damage sustained elsewhere in the panel.
It was concluded that Hybrid-3B results in a good trade-off between strength and stiffness and is advantageous over conventional CFRP and GFRP panels under a single blast load. Under repeated loading Hybrid-4 offers advantages over Hybrid-3B. Finally, the design of the support structure can significantly aid in blast resilience, and, a holistic approach considering both panels and support should be taken when designing for blast resilience.
Date Issued
2023-07
Date Acceptance
2023-05-14
Citation
Thin-Walled Structures, 2023, 188, pp.1-17
ISSN
0263-8231
Publisher
Elsevier BV
Start Page
1
End Page
17
Journal / Book Title
Thin-Walled Structures
Volume
188
Copyright Statement
© 2023 The Authors. Published by Elsevier Ltd. This is an open access article under the CC BY license
(http://creativecommons.org/licenses/by/4.0/).
(http://creativecommons.org/licenses/by/4.0/).
License URL
Identifier
http://dx.doi.org/10.1016/j.tws.2023.110874
Publication Status
Published
Article Number
110874
Date Publish Online
2023-06-03