Hydrogels derived from TEMPO-oxidised cellulose nanofibrils (TOCNs) are not robust and inherently water unstable if the
TOCNs are not crosslinked or coated with a water-swellable polymer. Furthermore, the manufacturing of self-standing TOCN
films is still a challenge due to the small TOCN diameter and viscosifying effect. Here, we report the TEMPO-mediated
oxidation of bacterial cellulose (BC) nanopaper as a route to produce robust and water stable TOCN hydrogel without the
need for additional additives or crosslinking steps, as well as self-standing TOCN films without the need for vacuum filtration
or slow-drying of TOCN suspension. Pristine BC pellicle was first press-dried into a dried and well-consolidated BC nanopaper,
followed by TEMPO-oxidation at various NaClO concentrations. The oxidation reaction introduced carboxylate moieties onto
exposed BC nanofibrils within the nanopaper network structure. This then led to the swelling of the nanopaper into a
hydrogel. A swelling ratio of up to 100 times the original thickness of BC nanopaper was observed upon TEMPO-oxidation.
The water retention value of the TEMPO-oxidised BC hydrogels was also found to increase with increasing carboxylate
content. These TEMPO-oxidised BC hydrogels were found to be robust and water-stable, even under prolonged (>1 month)
magnetic stirring in water. We further showed that high grammage self-standing TOCN films (100 g m-2) can be fabricated
as simple as press-drying a water stable TEMPO-oxidised BC hydrogels without the need of vacuum-assisted filtration or
slow-drying, which is typically the rate-limiting step in the manufacturing of self-standing TOCN films.